High Grade Body Shop Masking Tape


Professional high-performance masking tape with crepe paper backing and solvent based adhesive designed for automotive refinishing and nautical applications with high temperature drying cycles of up to 90°C (60 min.) or 110°C (30 min.). Particularly suitable when high adhesion is required and water-based paints are used. Performing perfectly well with masking paper and protective film and when used tape on tape. Thanks to its advanced formula, PPM Masking Tape 3010 adapts perfectly to irregular surfaces and can be removed without leaving adhesive residue on the application area. Suitable for uses on various surfaces, ensuring 3 days UV resistance.

FSC® and PEFC certified masking tapes available on demand.


Technical Data
  Metric Imperial Units Test Method
Total weight* 92 g/m2 92 g/m2 ISO 536
Total thickness* 125 μm 4.9 mils Internal
MD tensile strength* 38 N/cm 21.7 Lbs/in AFERA 5004/PSTC 131
MD elongation at break* 7 % 7 % AFERA 5004/PSTC 131
Adhesion to steel plate* 2.3 N/cm 21.0 oz/in AFERA 5001/PSTC 101
Service temperature up to
(1 hour)
90 °C 194°F  

*Typical Value

Backing material
Saturated Crepe Paper
Natural Rubber
Available colors
Medium/High adhesion
Excellent holding power
Suitable for most common water and solvent base paints
Clean removal after drying cycle at 90°C/194°F (max. 1 hour) — 110°C/230°F (max. 30 min)
Excellent adhesion on painted Metal, Rubber and Glass
Quick stick
Good paint anchorage
3 days UV resistance

Main applications

Recently Viewed Products

Privatelabel Home GIF (1)
Private Label

As a vertically integrated manufacturer with state-of-the-art production and converting facilities in Europe and Asia, we reliably produce the customized tape solution you need to streamline your business or compliment your portfolio. Talk to us. We are your strategic partner when it comes to manufacturing adhesive tapes.

Read more

Do you have any questions regarding PPM, our products or services?

Please write to us.
We will be glad to answer your enquiries.